AWS BAg-1a vs. N06219 Nickel

AWS BAg-1a belongs to the otherwise unclassified metals classification, while N06219 nickel belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-1a and the bottom bar is N06219 nickel.

AWS BAg-1a (P07500) Filler Metal UNS N06219 Nickel Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		77
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.33
Poisson's Ratio		0.29

Shear Modulus, GPa		29
Shear Modulus, GPa		79

Tensile Strength: Ultimate (UTS), MPa		180
Tensile Strength: Ultimate (UTS), MPa		730

Thermal Properties

Latent Heat of Fusion, J/g		120
Latent Heat of Fusion, J/g		330

Melting Completion (Liquidus), °C		640
Melting Completion (Liquidus), °C		1430

Melting Onset (Solidus), °C		630
Melting Onset (Solidus), °C		1380

Specific Heat Capacity, J/kg-K		280
Specific Heat Capacity, J/kg-K		450

Thermal Expansion, µm/m-K		22
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Density, g/cm³		9.3
Density, g/cm³		8.5

Embodied Carbon, kg CO₂/kg material		48
Embodied Carbon, kg CO₂/kg material		11

Embodied Energy, MJ/kg		760
Embodied Energy, MJ/kg		140

Common Calculations

Stiffness to Weight: Axial, points		4.6
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		15
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		5.4
Strength to Weight: Axial, points		24

Strength to Weight: Bending, points		7.6
Strength to Weight: Bending, points		21

Thermal Shock Resistance, points		7.5
Thermal Shock Resistance, points		21

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.5

Cadmium (Cd), %		17 to 19
Cadmium (Cd), %		0

Carbon (C), %		0
Carbon (C), %		0 to 0.050

Chromium (Cr), %		0
Chromium (Cr), %		18 to 22

Cobalt (Co), %		0
Cobalt (Co), %		0 to 1.0

Copper (Cu), %		14.5 to 16.5
Copper (Cu), %		0 to 0.5

Iron (Fe), %		0
Iron (Fe), %		2.0 to 4.0

Manganese (Mn), %		0
Manganese (Mn), %		0 to 0.5

Molybdenum (Mo), %		0
Molybdenum (Mo), %		7.0 to 9.0

Nickel (Ni), %		0
Nickel (Ni), %		60.8 to 72.3

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.020

Silicon (Si), %		0
Silicon (Si), %		0.7 to 1.1

Silver (Ag), %		49 to 51
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.010

Titanium (Ti), %		0
Titanium (Ti), %		0 to 0.5

Zinc (Zn), %		14.5 to 18.5
Zinc (Zn), %		0

Residuals, %		0 to 0.15
Residuals, %		0