AWS BAg-2 vs. C87800 Brass

AWS BAg-2 belongs to the otherwise unclassified metals classification, while C87800 brass belongs to the copper alloys. They have 40% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-2 and the bottom bar is C87800 brass.

AWS BAg-2 (P07350) Filler Metal UNS C87800 Silicon Brass

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		82
Elastic (Young's, Tensile) Modulus, GPa		110

Poisson's Ratio		0.32
Poisson's Ratio		0.33

Shear Modulus, GPa		31
Shear Modulus, GPa		42

Tensile Strength: Ultimate (UTS), MPa		180
Tensile Strength: Ultimate (UTS), MPa		590

Thermal Properties

Latent Heat of Fusion, J/g		130
Latent Heat of Fusion, J/g		260

Melting Completion (Liquidus), °C		700
Melting Completion (Liquidus), °C		920

Melting Onset (Solidus), °C		610
Melting Onset (Solidus), °C		820

Specific Heat Capacity, J/kg-K		310
Specific Heat Capacity, J/kg-K		410

Thermal Expansion, µm/m-K		22
Thermal Expansion, µm/m-K		18

Otherwise Unclassified Properties

Density, g/cm³		8.9
Density, g/cm³		8.3

Embodied Carbon, kg CO₂/kg material		35
Embodied Carbon, kg CO₂/kg material		2.7

Embodied Energy, MJ/kg		550
Embodied Energy, MJ/kg		44

Common Calculations

Stiffness to Weight: Axial, points		5.1
Stiffness to Weight: Axial, points		7.4

Stiffness to Weight: Bending, points		16
Stiffness to Weight: Bending, points		19

Strength to Weight: Axial, points		5.6
Strength to Weight: Axial, points		20

Strength to Weight: Bending, points		7.9
Strength to Weight: Bending, points		19

Thermal Shock Resistance, points		7.0
Thermal Shock Resistance, points		21

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.15

Antimony (Sb), %		0
Antimony (Sb), %		0 to 0.050

Arsenic (As), %		0
Arsenic (As), %		0 to 0.050

Cadmium (Cd), %		17 to 19
Cadmium (Cd), %		0

Copper (Cu), %		25 to 27
Copper (Cu), %		80 to 84.2

Iron (Fe), %		0
Iron (Fe), %		0 to 0.15

Lead (Pb), %		0
Lead (Pb), %		0 to 0.15

Magnesium (Mg), %		0
Magnesium (Mg), %		0 to 0.010

Manganese (Mn), %		0
Manganese (Mn), %		0 to 0.15

Nickel (Ni), %		0
Nickel (Ni), %		0 to 0.2

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.010

Silicon (Si), %		0
Silicon (Si), %		3.8 to 4.2

Silver (Ag), %		34 to 36
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.050

Tin (Sn), %		0
Tin (Sn), %		0 to 0.25

Zinc (Zn), %		19 to 23
Zinc (Zn), %		12 to 16

Residuals, %		0
Residuals, %		0 to 0.5