AWS BAg-2 vs. N08026 Nickel

AWS BAg-2 belongs to the otherwise unclassified metals classification, while N08026 nickel belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-2 and the bottom bar is N08026 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
200
Poisson's Ratio 0.32
0.28
Shear Modulus, GPa 31
80
Tensile Strength: Ultimate (UTS), MPa 180
620

Thermal Properties

Latent Heat of Fusion, J/g 130
310
Melting Completion (Liquidus), °C 700
1430
Melting Onset (Solidus), °C 610
1380
Specific Heat Capacity, J/kg-K 310
460
Thermal Expansion, µm/m-K 22
15

Otherwise Unclassified Properties

Density, g/cm3 8.9
8.2
Embodied Carbon, kg CO2/kg material 35
7.2
Embodied Energy, MJ/kg 550
98

Common Calculations

Stiffness to Weight: Axial, points 5.1
14
Stiffness to Weight: Bending, points 16
24
Strength to Weight: Axial, points 5.6
21
Strength to Weight: Bending, points 7.9
20
Thermal Shock Resistance, points 7.0
15

Alloy Composition

Cadmium (Cd), % 17 to 19
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
22 to 26
Copper (Cu), % 25 to 27
2.0 to 4.0
Iron (Fe), % 0
24.4 to 37.9
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
5.0 to 6.7
Nickel (Ni), % 0
33 to 37.2
Nitrogen (N), % 0
0.1 to 0.16
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 34 to 36
0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 19 to 23
0
Residuals, % 0 to 0.15
0