AWS BAg-21 vs. C49300 Brass

AWS BAg-21 belongs to the otherwise unclassified metals classification, while C49300 brass belongs to the copper alloys. They have a modest 31% of their average alloy composition in common, which, by itself, doesn't mean much. There are 16 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-21 and the bottom bar is C49300 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 85
100
Poisson's Ratio 0.36
0.31
Shear Modulus, GPa 31
40
Tensile Strength: Ultimate (UTS), MPa 150
430 to 520

Thermal Properties

Latent Heat of Fusion, J/g 140
170
Melting Completion (Liquidus), °C 800
880
Melting Onset (Solidus), °C 690
840
Specific Heat Capacity, J/kg-K 280
380
Thermal Expansion, µm/m-K 19
20

Otherwise Unclassified Properties

Density, g/cm3 9.8
8.0
Embodied Energy, MJ/kg 970
50

Common Calculations

Stiffness to Weight: Axial, points 4.8
7.2
Stiffness to Weight: Bending, points 15
19
Strength to Weight: Axial, points 4.2
15 to 18
Strength to Weight: Bending, points 6.4
16 to 18
Thermal Shock Resistance, points 6.6
14 to 18

Alloy Composition

Aluminum (Al), % 0
0 to 0.5
Antimony (Sb), % 0
0 to 0.5
Bismuth (Bi), % 0
0.5 to 2.0
Copper (Cu), % 27.5 to 29.5
58 to 62
Iron (Fe), % 0
0 to 0.1
Lead (Pb), % 0
0 to 0.010
Manganese (Mn), % 0
0 to 0.030
Nickel (Ni), % 2.0 to 3.0
0 to 1.5
Phosphorus (P), % 0
0 to 0.2
Selenium (Se), % 0
0 to 0.2
Silicon (Si), % 0
0 to 0.1
Silver (Ag), % 62 to 64
0
Tin (Sn), % 5.0 to 7.0
1.0 to 1.8
Zinc (Zn), % 0
30.6 to 40.5
Residuals, % 0
0 to 0.5