AWS BAg-22 vs. AWS BNi-8

AWS BAg-22 belongs to the otherwise unclassified metals classification, while AWS BNi-8 belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-22 and the bottom bar is AWS BNi-8.

AWS BAg-22 (P07490) Filler Metal AWS BNi-8 (N99800) Filler Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		96
Elastic (Young's, Tensile) Modulus, GPa		180

Poisson's Ratio		0.33
Poisson's Ratio		0.32

Shear Modulus, GPa		36
Shear Modulus, GPa		67

Tensile Strength: Ultimate (UTS), MPa		140
Tensile Strength: Ultimate (UTS), MPa		570

Thermal Properties

Brazing Temperature, °C		700 to 1040
Brazing Temperature, °C		1010 to 1090

Latent Heat of Fusion, J/g		150
Latent Heat of Fusion, J/g		390

Melting Completion (Liquidus), °C		700
Melting Completion (Liquidus), °C		1010

Melting Onset (Solidus), °C		680
Melting Onset (Solidus), °C		980

Specific Heat Capacity, J/kg-K		320
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		21
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Density, g/cm³		9.0
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		48
Embodied Carbon, kg CO₂/kg material		8.2

Embodied Energy, MJ/kg		760
Embodied Energy, MJ/kg		120

Common Calculations

Stiffness to Weight: Axial, points		5.9
Stiffness to Weight: Axial, points		12

Stiffness to Weight: Bending, points		17
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		4.3
Strength to Weight: Axial, points		20

Strength to Weight: Bending, points		6.6
Strength to Weight: Bending, points		19

Thermal Shock Resistance, points		5.1
Thermal Shock Resistance, points		17

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.050

Carbon (C), %		0
Carbon (C), %		0 to 0.060

Cobalt (Co), %		0
Cobalt (Co), %		0 to 0.1

Copper (Cu), %		15 to 17
Copper (Cu), %		4.0 to 5.0

Manganese (Mn), %		7.0 to 8.0
Manganese (Mn), %		21.5 to 24.5

Nickel (Ni), %		4.0 to 5.0
Nickel (Ni), %		61.6 to 68.5

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.020

Selenium (Se), %		0
Selenium (Se), %		0 to 0.0050

Silicon (Si), %		0
Silicon (Si), %		6.0 to 8.0

Silver (Ag), %		48 to 50
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.020

Titanium (Ti), %		0
Titanium (Ti), %		0 to 0.050

Zinc (Zn), %		21 to 25
Zinc (Zn), %		0

Zirconium (Zr), %		0
Zirconium (Zr), %		0 to 0.050

Residuals, %		0
Residuals, %		0 to 0.5