AWS BAg-22 vs. N06007 Nickel

AWS BAg-22 belongs to the otherwise unclassified metals classification, while N06007 nickel belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-22 and the bottom bar is N06007 nickel.

AWS BAg-22 (P07490) Filler Metal UNS N06007 (2.4618) Nickel Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		96
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.33
Poisson's Ratio		0.29

Shear Modulus, GPa		36
Shear Modulus, GPa		79

Tensile Strength: Ultimate (UTS), MPa		140
Tensile Strength: Ultimate (UTS), MPa		690

Thermal Properties

Latent Heat of Fusion, J/g		150
Latent Heat of Fusion, J/g		320

Melting Completion (Liquidus), °C		700
Melting Completion (Liquidus), °C		1340

Melting Onset (Solidus), °C		680
Melting Onset (Solidus), °C		1260

Specific Heat Capacity, J/kg-K		320
Specific Heat Capacity, J/kg-K		450

Thermal Expansion, µm/m-K		21
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Density, g/cm³		9.0
Density, g/cm³		8.4

Embodied Carbon, kg CO₂/kg material		48
Embodied Carbon, kg CO₂/kg material		10

Embodied Energy, MJ/kg		760
Embodied Energy, MJ/kg		140

Common Calculations

Stiffness to Weight: Axial, points		5.9
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		17
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		4.3
Strength to Weight: Axial, points		23

Strength to Weight: Bending, points		6.6
Strength to Weight: Bending, points		21

Thermal Shock Resistance, points		5.1
Thermal Shock Resistance, points		18

Alloy Composition

Carbon (C), %		0
Carbon (C), %		0 to 0.050

Chromium (Cr), %		0
Chromium (Cr), %		21 to 23.5

Cobalt (Co), %		0
Cobalt (Co), %		0 to 2.5

Copper (Cu), %		15 to 17
Copper (Cu), %		1.5 to 2.5

Iron (Fe), %		0
Iron (Fe), %		18 to 21

Manganese (Mn), %		7.0 to 8.0
Manganese (Mn), %		1.0 to 2.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		5.5 to 7.5

Nickel (Ni), %		4.0 to 5.0
Nickel (Ni), %		36.1 to 51.1

Niobium (Nb), %		0
Niobium (Nb), %		1.8 to 2.5

Nitrogen (N), %		0
Nitrogen (N), %		0.15 to 0.25

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0
Silicon (Si), %		0 to 1.0

Silver (Ag), %		48 to 50
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030

Tungsten (W), %		0
Tungsten (W), %		0 to 1.0

Zinc (Zn), %		21 to 25
Zinc (Zn), %		0

Residuals, %		0 to 0.15
Residuals, %		0