AWS BAg-24 vs. EN 1.8824 Steel

AWS BAg-24 belongs to the otherwise unclassified metals classification, while EN 1.8824 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-24 and the bottom bar is EN 1.8824 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
190
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 33
73
Tensile Strength: Ultimate (UTS), MPa 150
580

Thermal Properties

Latent Heat of Fusion, J/g 130
250
Melting Completion (Liquidus), °C 730
1460
Melting Onset (Solidus), °C 660
1420
Specific Heat Capacity, J/kg-K 310
470
Thermal Expansion, µm/m-K 21
13

Otherwise Unclassified Properties

Density, g/cm3 9.0
7.8
Embodied Carbon, kg CO2/kg material 49
1.6
Embodied Energy, MJ/kg 770
21

Common Calculations

Stiffness to Weight: Axial, points 5.3
13
Stiffness to Weight: Bending, points 16
24
Strength to Weight: Axial, points 4.6
21
Strength to Weight: Bending, points 6.9
20
Thermal Shock Resistance, points 5.9
17

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.040
Carbon (C), % 0
0 to 0.16
Copper (Cu), % 19 to 21
0
Iron (Fe), % 0
96.6 to 99.98
Manganese (Mn), % 0
0 to 1.7
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 1.5 to 2.5
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 49 to 51
0
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.1
Zinc (Zn), % 26 to 30
0
Residuals, % 0 to 0.15
0