AWS BAg-26 belongs to the otherwise unclassified metals classification, while CC481K bronze belongs to the copper alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-26 and the bottom bar is CC481K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
110
Poisson's Ratio 0.32
0.34
Shear Modulus, GPa 37
40
Tensile Strength: Ultimate (UTS), MPa 160
350

Thermal Properties

Latent Heat of Fusion, J/g 160
190
Melting Completion (Liquidus), °C 800
1000
Melting Onset (Solidus), °C 710
880
Specific Heat Capacity, J/kg-K 350
370
Thermal Expansion, µm/m-K 21
18

Otherwise Unclassified Properties

Density, g/cm3 8.5
8.7
Embodied Carbon, kg CO2/kg material 26
3.7
Embodied Energy, MJ/kg 410
60

Common Calculations

Stiffness to Weight: Axial, points 6.4
6.9
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 5.2
11
Strength to Weight: Bending, points 7.7
13
Thermal Shock Resistance, points 5.6
13

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.050
Copper (Cu), % 37 to 39
87 to 89.5
Iron (Fe), % 0
0 to 0.1
Lead (Pb), % 0
0 to 0.25
Manganese (Mn), % 1.5 to 2.5
0 to 0.050
Nickel (Ni), % 1.5 to 2.5
0 to 0.1
Phosphorus (P), % 0
0 to 1.0
Silicon (Si), % 0
0 to 0.010
Silver (Ag), % 24 to 26
0
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0
10 to 11.5
Zinc (Zn), % 31 to 35
0 to 0.5
Residuals, % 0 to 0.15
0