AWS BAg-2a vs. ASTM A216 Cast Steel
AWS BAg-2a belongs to the otherwise unclassified metals classification, while ASTM A216 cast steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is AWS BAg-2a and the bottom bar is ASTM A216 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 83 | |
190 |
Poisson's Ratio | 0.32 | |
0.29 |
Shear Modulus, GPa | 31 | |
72 |
Tensile Strength: Ultimate (UTS), MPa | 170 | |
500 to 570 |
Thermal Properties
Latent Heat of Fusion, J/g | 130 | |
250 |
Melting Completion (Liquidus), °C | 710 | |
1450 to 1460 |
Melting Onset (Solidus), °C | 610 | |
1410 |
Specific Heat Capacity, J/kg-K | 310 | |
470 |
Thermal Expansion, µm/m-K | 23 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 30 | |
1.4 |
Embodied Energy, MJ/kg | 470 | |
18 |
Common Calculations
Stiffness to Weight: Axial, points | 5.2 | |
13 |
Stiffness to Weight: Bending, points | 17 | |
24 |
Strength to Weight: Axial, points | 5.4 | |
18 to 20 |
Strength to Weight: Bending, points | 7.8 | |
18 to 20 |
Thermal Shock Resistance, points | 6.5 | |
16 to 18 |