AWS BAg-3 vs. ASTM B563 Pd-Ag-Cu
Both AWS BAg-3 and ASTM B563 Pd-Ag-Cu are otherwise unclassified metals. They have 55% of their average alloy composition in common. There are 15 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is AWS BAg-3 and the bottom bar is ASTM B563 Pd-Ag-Cu.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 80 | |
| 100 |
| Poisson's Ratio | 0.33 | |
| 0.37 |
| Shear Modulus, GPa | 30 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 170 | |
| 760 to 1170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 120 | |
| 150 |
| Melting Completion (Liquidus), °C | 690 | |
| 1180 |
| Melting Onset (Solidus), °C | 630 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 290 | |
| 260 |
| Thermal Expansion, µm/m-K | 22 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.3 | |
| 11 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.8 | |
| 5.2 |
| Stiffness to Weight: Bending, points | 15 | |
| 14 |
| Strength to Weight: Axial, points | 5.1 | |
| 19 to 30 |
| Strength to Weight: Bending, points | 7.3 | |
| 17 to 22 |
| Thermal Shock Resistance, points | 6.9 | |
| 39 to 61 |
Alloy Composition
| Cadmium (Cd), % | 15 to 17 | |
| 0 |
| Copper (Cu), % | 14.5 to 16.5 | |
| 15.5 to 16.5 |
| Nickel (Ni), % | 2.5 to 3.5 | |
| 0.8 to 1.2 |
| Palladium (Pd), % | 0 | |
| 43 to 45 |
| Platinum (Pt), % | 0 | |
| 0.8 to 1.2 |
| Silver (Ag), % | 49 to 51 | |
| 37 to 39 |
| Zinc (Zn), % | 13.5 to 17.5 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |