AWS BAg-3 vs. ASTM B628 Ag-Cu
Both AWS BAg-3 and ASTM B628 Ag-Cu are otherwise unclassified metals. They have 66% of their average alloy composition in common. There are 15 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is AWS BAg-3 and the bottom bar is ASTM B628 Ag-Cu.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 80 | |
| 83 |
| Poisson's Ratio | 0.33 | |
| 0.36 |
| Shear Modulus, GPa | 30 | |
| 31 |
| Tensile Strength: Ultimate (UTS), MPa | 170 | |
| 350 to 760 |
Thermal Properties
| Latent Heat of Fusion, J/g | 120 | |
| 140 |
| Melting Completion (Liquidus), °C | 690 | |
| 780 |
| Melting Onset (Solidus), °C | 630 | |
| 780 |
| Specific Heat Capacity, J/kg-K | 290 | |
| 280 |
| Thermal Expansion, µm/m-K | 22 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.3 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.8 | |
| 4.6 |
| Stiffness to Weight: Bending, points | 15 | |
| 14 |
| Strength to Weight: Axial, points | 5.1 | |
| 9.5 to 21 |
| Strength to Weight: Bending, points | 7.3 | |
| 11 to 18 |
| Thermal Shock Resistance, points | 6.9 | |
| 16 to 34 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Cadmium (Cd), % | 15 to 17 | |
| 0 to 0.050 |
| Copper (Cu), % | 14.5 to 16.5 | |
| 26.6 to 29 |
| Iron (Fe), % | 0 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.030 |
| Nickel (Ni), % | 2.5 to 3.5 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silver (Ag), % | 49 to 51 | |
| 71 to 73 |
| Zinc (Zn), % | 13.5 to 17.5 | |
| 0 to 0.060 |
| Residuals, % | 0 | |
| 0 to 0.21 |