AWS BAg-3 vs. AWS BAg-13
Both AWS BAg-3 and AWS BAg-13 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 72% of their average alloy composition in common.
For each property being compared, the top bar is AWS BAg-3 and the bottom bar is AWS BAg-13.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 80 | |
| 91 |
| Poisson's Ratio | 0.33 | |
| 0.35 |
| Shear Modulus, GPa | 30 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 170 | |
| 180 |
Thermal Properties
| Brazing Temperature, °C | 690 to 900 | |
| 860 to 980 |
| Latent Heat of Fusion, J/g | 120 | |
| 150 |
| Melting Completion (Liquidus), °C | 690 | |
| 860 |
| Melting Onset (Solidus), °C | 630 | |
| 720 |
| Specific Heat Capacity, J/kg-K | 290 | |
| 310 |
| Thermal Expansion, µm/m-K | 22 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.3 | |
| 9.7 |
| Embodied Carbon, kg CO2/kg material | 49 | |
| 52 |
| Embodied Energy, MJ/kg | 770 | |
| 820 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.8 | |
| 5.2 |
| Stiffness to Weight: Bending, points | 15 | |
| 16 |
| Strength to Weight: Axial, points | 5.1 | |
| 5.2 |
| Strength to Weight: Bending, points | 7.3 | |
| 7.3 |
| Thermal Shock Resistance, points | 6.9 | |
| 7.5 |
Alloy Composition
| Cadmium (Cd), % | 15 to 17 | |
| 0 |
| Copper (Cu), % | 14.5 to 16.5 | |
| 37.4 to 42.5 |
| Nickel (Ni), % | 2.5 to 3.5 | |
| 0.5 to 1.5 |
| Silver (Ag), % | 49 to 51 | |
| 53 to 55 |
| Zinc (Zn), % | 13.5 to 17.5 | |
| 4.0 to 6.0 |
| Residuals, % | 0 | |
| 0 to 0.15 |