AWS BAg-3 vs. AWS BAg-27
Both AWS BAg-3 and AWS BAg-27 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 70% of their average alloy composition in common.
For each property being compared, the top bar is AWS BAg-3 and the bottom bar is AWS BAg-27.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 80 | |
| 88 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 30 | |
| 33 |
| Tensile Strength: Ultimate (UTS), MPa | 170 | |
| 160 |
Thermal Properties
| Brazing Temperature, °C | 690 to 900 | |
| 710 to 860 |
| Latent Heat of Fusion, J/g | 120 | |
| 140 |
| Melting Completion (Liquidus), °C | 690 | |
| 750 |
| Melting Onset (Solidus), °C | 630 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 290 | |
| 330 |
| Thermal Expansion, µm/m-K | 22 | |
| 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.3 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 49 | |
| 25 |
| Embodied Energy, MJ/kg | 770 | |
| 400 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.8 | |
| 5.7 |
| Stiffness to Weight: Bending, points | 15 | |
| 17 |
| Strength to Weight: Axial, points | 5.1 | |
| 5.1 |
| Strength to Weight: Bending, points | 7.3 | |
| 7.6 |
| Thermal Shock Resistance, points | 6.9 | |
| 5.9 |
Alloy Composition
| Cadmium (Cd), % | 15 to 17 | |
| 12.5 to 14.5 |
| Copper (Cu), % | 14.5 to 16.5 | |
| 34 to 36 |
| Nickel (Ni), % | 2.5 to 3.5 | |
| 0 |
| Silver (Ag), % | 49 to 51 | |
| 24 to 26 |
| Zinc (Zn), % | 13.5 to 17.5 | |
| 24.5 to 28.5 |
| Residuals, % | 0 | |
| 0 to 0.15 |