AWS BAg-3 vs. Z40101 Zinc
AWS BAg-3 belongs to the otherwise unclassified metals classification, while Z40101 zinc belongs to the zinc alloys. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is AWS BAg-3 and the bottom bar is Z40101 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 80 | |
| 87 |
| Poisson's Ratio | 0.33 | |
| 0.25 |
| Shear Modulus, GPa | 30 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 170 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 120 | |
| 110 |
| Melting Completion (Liquidus), °C | 690 | |
| 410 |
| Melting Onset (Solidus), °C | 630 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 290 | |
| 390 |
| Thermal Expansion, µm/m-K | 22 | |
| 26 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.3 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 49 | |
| 2.8 |
| Embodied Energy, MJ/kg | 770 | |
| 53 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.8 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 15 | |
| 23 |
| Strength to Weight: Axial, points | 5.1 | |
| 5.7 |
| Strength to Weight: Bending, points | 7.3 | |
| 8.9 |
| Thermal Shock Resistance, points | 6.9 | |
| 4.2 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Cadmium (Cd), % | 15 to 17 | |
| 0 to 0.0050 |
| Copper (Cu), % | 14.5 to 16.5 | |
| 0.080 to 0.4 |
| Iron (Fe), % | 0 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 | |
| 0 to 0.010 |
| Nickel (Ni), % | 2.5 to 3.5 | |
| 0 |
| Silver (Ag), % | 49 to 51 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Titanium (Ti), % | 0 | |
| 0 to 0.020 |
| Zinc (Zn), % | 13.5 to 17.5 | |
| 99.542 to 99.92 |
| Residuals, % | 0 to 0.15 | |
| 0 |