AWS BAg-36 vs. SAE-AISI M3 Class 1 Steel

AWS BAg-36 belongs to the otherwise unclassified metals classification, while SAE-AISI M3 class 1 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-36 and the bottom bar is SAE-AISI M3 class 1 steel.

AWS BAg-36 (P07454) Filler Metal SAE-AISI M3 Class 1 (T11313) Molybdenum High-Speed Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		86
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.33
Poisson's Ratio		0.29

Shear Modulus, GPa		32
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		160
Tensile Strength: Ultimate (UTS), MPa		770 to 2150

Thermal Properties

Latent Heat of Fusion, J/g		140
Latent Heat of Fusion, J/g		260

Melting Completion (Liquidus), °C		680
Melting Completion (Liquidus), °C		1610

Melting Onset (Solidus), °C		650
Melting Onset (Solidus), °C		1570

Specific Heat Capacity, J/kg-K		310
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		21
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Density, g/cm³		9.0
Density, g/cm³		8.3

Embodied Carbon, kg CO₂/kg material		44
Embodied Carbon, kg CO₂/kg material		10

Embodied Energy, MJ/kg		700
Embodied Energy, MJ/kg		150

Common Calculations

Stiffness to Weight: Axial, points		5.3
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		16
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		4.9
Strength to Weight: Axial, points		26 to 72

Strength to Weight: Bending, points		7.3
Strength to Weight: Bending, points		22 to 44

Thermal Shock Resistance, points		6.4
Thermal Shock Resistance, points		24 to 67

Alloy Composition

Carbon (C), %		0
Carbon (C), %		1.0 to 1.1

Chromium (Cr), %		0
Chromium (Cr), %		3.8 to 4.5

Copper (Cu), %		26 to 28
Copper (Cu), %		0 to 0.25

Iron (Fe), %		0
Iron (Fe), %		76.9 to 82.9

Manganese (Mn), %		0
Manganese (Mn), %		0.15 to 0.4

Molybdenum (Mo), %		0
Molybdenum (Mo), %		4.8 to 6.5

Nickel (Ni), %		0
Nickel (Ni), %		0 to 0.3

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0
Silicon (Si), %		0.2 to 0.45

Silver (Ag), %		44 to 46
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030

Tin (Sn), %		2.5 to 3.5
Tin (Sn), %		0

Tungsten (W), %		0
Tungsten (W), %		5.0 to 6.8

Vanadium (V), %		0
Vanadium (V), %		2.3 to 2.8

Zinc (Zn), %		23 to 27
Zinc (Zn), %		0

Residuals, %		0 to 0.15
Residuals, %		0