AWS BAg-4 vs. N06110 Nickel

AWS BAg-4 belongs to the otherwise unclassified metals classification, while N06110 nickel belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-4 and the bottom bar is N06110 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 91
210
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 34
84
Tensile Strength: Ultimate (UTS), MPa 150
730

Thermal Properties

Latent Heat of Fusion, J/g 140
340
Melting Completion (Liquidus), °C 780
1490
Melting Onset (Solidus), °C 670
1440
Specific Heat Capacity, J/kg-K 330
440
Thermal Expansion, µm/m-K 21
12

Otherwise Unclassified Properties

Density, g/cm3 8.9
8.6
Embodied Carbon, kg CO2/kg material 40
11
Embodied Energy, MJ/kg 630
160

Common Calculations

Stiffness to Weight: Axial, points 5.7
14
Stiffness to Weight: Bending, points 17
23
Strength to Weight: Axial, points 4.7
23
Strength to Weight: Bending, points 7.1
21
Thermal Shock Resistance, points 5.7
20

Alloy Composition

Aluminum (Al), % 0
0 to 1.0
Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
28 to 33
Copper (Cu), % 29 to 31
0 to 0.5
Iron (Fe), % 0
0 to 1.0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
9.0 to 12
Nickel (Ni), % 1.5 to 2.5
51 to 62
Niobium (Nb), % 0
0 to 1.0
Phosphorus (P), % 0
0 to 0.5
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 39 to 41
0
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 0
0 to 1.0
Tungsten (W), % 0
1.0 to 4.0
Zinc (Zn), % 26 to 30
0
Residuals, % 0 to 0.15
0