AWS BAg-5 vs. EN 1.7378 Steel

AWS BAg-5 belongs to the otherwise unclassified metals classification, while EN 1.7378 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-5 and the bottom bar is EN 1.7378 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 88
190
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 33
74
Tensile Strength: Ultimate (UTS), MPa 150
700

Thermal Properties

Latent Heat of Fusion, J/g 140
260
Melting Completion (Liquidus), °C 740
1470
Melting Onset (Solidus), °C 660
1430
Specific Heat Capacity, J/kg-K 320
470
Thermal Expansion, µm/m-K 21
13

Otherwise Unclassified Properties

Density, g/cm3 9.0
7.8
Embodied Carbon, kg CO2/kg material 44
2.3
Embodied Energy, MJ/kg 700
33

Common Calculations

Stiffness to Weight: Axial, points 5.4
13
Stiffness to Weight: Bending, points 16
24
Strength to Weight: Axial, points 4.6
25
Strength to Weight: Bending, points 6.9
22
Thermal Shock Resistance, points 5.9
20

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0.0015 to 0.0070
Carbon (C), % 0
0.050 to 0.1
Chromium (Cr), % 0
2.2 to 2.6
Copper (Cu), % 29 to 31
0
Iron (Fe), % 0
94.6 to 96.1
Manganese (Mn), % 0
0.3 to 0.7
Molybdenum (Mo), % 0
0.9 to 1.1
Nitrogen (N), % 0
0 to 0.010
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0.15 to 0.45
Silver (Ag), % 44 to 46
0
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0
0.050 to 0.1
Vanadium (V), % 0
0.2 to 0.3
Zinc (Zn), % 23 to 27
0
Residuals, % 0 to 0.15
0