Both AWS BAg-6 and AWS BVAg-32 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 71% of their average alloy composition in common. There are 16 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is AWS BVAg-32.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
93
Poisson's Ratio 0.34
0.37
Shear Modulus, GPa 33
34
Tensile Strength: Ultimate (UTS), MPa 160
180

Thermal Properties

Brazing Temperature, °C 650 to 870
950 to 980
Latent Heat of Fusion, J/g 140
140
Melting Completion (Liquidus), °C 770
950
Melting Onset (Solidus), °C 690
900
Specific Heat Capacity, J/kg-K 310
270
Thermal Expansion, µm/m-K 20
17

Otherwise Unclassified Properties

Density, g/cm3 9.3
11

Common Calculations

Stiffness to Weight: Axial, points 5.3
4.9
Stiffness to Weight: Bending, points 16
14
Strength to Weight: Axial, points 4.8
4.7
Strength to Weight: Bending, points 7.0
6.7
Thermal Shock Resistance, points 6.5
8.0

Alloy Composition

Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0
0 to 0.0050
Copper (Cu), % 33 to 35
20 to 22
Lead (Pb), % 0
0 to 0.0020
Palladium (Pd), % 0
23 to 27
Phosphorus (P), % 0
0 to 0.0020
Silver (Ag), % 49 to 51
53 to 55
Zinc (Zn), % 14 to 18
0 to 0.0010
Residuals, % 0 to 0.15
0