MakeItFrom.com
Menu (ESC)

AWS BAg-8a vs. EN 1.8872 Steel

AWS BAg-8a belongs to the otherwise unclassified metals classification, while EN 1.8872 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-8a and the bottom bar is EN 1.8872 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
190
Poisson's Ratio 0.36
0.29
Shear Modulus, GPa 31
73
Tensile Strength: Ultimate (UTS), MPa 150
610

Thermal Properties

Latent Heat of Fusion, J/g 140
250
Melting Completion (Liquidus), °C 770
1460
Melting Onset (Solidus), °C 770
1420
Specific Heat Capacity, J/kg-K 290
470
Thermal Expansion, µm/m-K 19
13

Otherwise Unclassified Properties

Density, g/cm3 10
7.9

Common Calculations

Stiffness to Weight: Axial, points 4.6
13
Stiffness to Weight: Bending, points 15
24
Strength to Weight: Axial, points 4.2
22
Strength to Weight: Bending, points 6.3
20
Thermal Shock Resistance, points 6.7
18

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0
0 to 0.18
Chromium (Cr), % 0
0 to 0.5
Copper (Cu), % 26.4 to 28.8
0 to 0.3
Iron (Fe), % 0
95.1 to 100
Lithium (Li), % 0.25 to 0.5
0
Manganese (Mn), % 0
0 to 1.7
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
0 to 1.0
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 71 to 73
0
Sulfur (S), % 0
0 to 0.0080
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.080
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0 to 0.15
0