AWS BAg-8a vs. N06002 Nickel

AWS BAg-8a belongs to the otherwise unclassified metals classification, while N06002 nickel belongs to the nickel alloys. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-8a and the bottom bar is N06002 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
210
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 31
81
Tensile Strength: Ultimate (UTS), MPa 150
760

Thermal Properties

Latent Heat of Fusion, J/g 140
320
Melting Completion (Liquidus), °C 770
1360
Melting Onset (Solidus), °C 770
1260
Specific Heat Capacity, J/kg-K 290
450
Thermal Expansion, µm/m-K 19
14

Otherwise Unclassified Properties

Density, g/cm3 10
8.5

Common Calculations

Stiffness to Weight: Axial, points 4.6
14
Stiffness to Weight: Bending, points 15
23
Strength to Weight: Axial, points 4.2
25
Strength to Weight: Bending, points 6.3
22
Thermal Shock Resistance, points 6.7
19

Alloy Composition

Carbon (C), % 0
0.050 to 0.15
Chromium (Cr), % 0
20.5 to 23
Cobalt (Co), % 0
0.5 to 2.5
Copper (Cu), % 26.4 to 28.8
0
Iron (Fe), % 0
17 to 20
Lithium (Li), % 0.25 to 0.5
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 0
42.3 to 54
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 71 to 73
0
Sulfur (S), % 0
0 to 0.030
Tungsten (W), % 0
0.2 to 1.0
Residuals, % 0 to 0.15
0