AWS BAg-9 vs. Solder Alloy 503
Both AWS BAg-9 and solder alloy 503 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 16 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is AWS BAg-9 and the bottom bar is solder alloy 503.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 82 | |
| 54 |
| Poisson's Ratio | 0.35 | |
| 0.36 |
| Shear Modulus, GPa | 31 | |
| 20 |
| Tensile Strength: Ultimate (UTS), MPa | 140 | |
| 57 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 69 |
| Melting Completion (Liquidus), °C | 720 | |
| 380 |
| Melting Onset (Solidus), °C | 670 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 290 | |
| 230 |
| Thermal Expansion, µm/m-K | 20 | |
| 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.6 | |
| 7.5 |
| Embodied Energy, MJ/kg | 980 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.8 | |
| 4.1 |
| Stiffness to Weight: Bending, points | 15 | |
| 17 |
| Strength to Weight: Axial, points | 4.1 | |
| 2.1 |
| Strength to Weight: Bending, points | 6.3 | |
| 4.4 |
| Thermal Shock Resistance, points | 6.0 | |
| 3.5 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.1 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.080 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Copper (Cu), % | 19 to 21 | |
| 5.5 to 6.5 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 | |
| 0 to 0.070 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 64 to 66 | |
| 1.8 to 2.2 |
| Tin (Sn), % | 0 | |
| 90.8 to 92.7 |
| Zinc (Zn), % | 13 to 17 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.15 | |
| 0 |