AWS BAu-2 vs. EN 1.7367 Steel

AWS BAu-2 belongs to the otherwise unclassified metals classification, while EN 1.7367 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS BAu-2 and the bottom bar is EN 1.7367 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
190
Poisson's Ratio 0.4
0.28
Shear Modulus, GPa 36
75
Tensile Strength: Ultimate (UTS), MPa 150
670

Thermal Properties

Latent Heat of Fusion, J/g 92
270
Melting Completion (Liquidus), °C 890
1460
Melting Onset (Solidus), °C 890
1420
Specific Heat Capacity, J/kg-K 180
470
Thermal Expansion, µm/m-K 15
13

Otherwise Unclassified Properties

Density, g/cm3 17
7.8

Common Calculations

Stiffness to Weight: Axial, points 3.3
14
Stiffness to Weight: Bending, points 9.1
25
Strength to Weight: Axial, points 2.4
24
Strength to Weight: Bending, points 3.6
22
Thermal Shock Resistance, points 7.1
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Carbon (C), % 0
0.080 to 0.12
Chromium (Cr), % 0
8.0 to 9.5
Copper (Cu), % 19.4 to 20.5
0
Gold (Au), % 79.5 to 80.5
0
Iron (Fe), % 0
87.3 to 90.3
Manganese (Mn), % 0
0.3 to 0.6
Molybdenum (Mo), % 0
0.85 to 1.1
Nickel (Ni), % 0
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.2 to 0.5
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Vanadium (V), % 0
0.18 to 0.25
Zirconium (Zr), % 0
0 to 0.010
Residuals, % 0 to 0.15
0