AWS BAu-2 vs. Reactor Grade Zirconium
Both AWS BAu-2 and reactor grade zirconium are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AWS BAu-2 and the bottom bar is reactor grade zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 98 |
| Poisson's Ratio | 0.4 | |
| 0.34 |
| Shear Modulus, GPa | 36 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 150 | |
| 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 92 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 180 | |
| 270 |
| Thermal Expansion, µm/m-K | 15 | |
| 5.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 6.5 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.3 | |
| 8.4 |
| Stiffness to Weight: Bending, points | 9.1 | |
| 24 |
| Strength to Weight: Axial, points | 2.4 | |
| 14 |
| Strength to Weight: Bending, points | 3.6 | |
| 16 |
| Thermal Shock Resistance, points | 7.1 | |
| 41 |
Alloy Composition
| Copper (Cu), % | 19.4 to 20.5 | |
| 0 |
| Gold (Au), % | 79.5 to 80.5 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 99.7 to 100 |
| Residuals, % | 0 | |
| 0 to 0.27 |