AWS BAu-6 vs. C63800 Bronze
AWS BAu-6 belongs to the otherwise unclassified metals classification, while C63800 bronze belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is AWS BAu-6 and the bottom bar is C63800 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Poisson's Ratio | 0.39 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 190 | |
| 460 to 1010 |
Thermal Properties
| Latent Heat of Fusion, J/g | 120 | |
| 240 |
| Melting Completion (Liquidus), °C | 1050 | |
| 1030 |
| Melting Onset (Solidus), °C | 1010 | |
| 1000 |
| Specific Heat Capacity, J/kg-K | 210 | |
| 410 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 16 | |
| 8.6 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.0 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 10 | |
| 19 |
| Strength to Weight: Axial, points | 3.2 | |
| 15 to 33 |
| Strength to Weight: Bending, points | 4.5 | |
| 15 to 26 |
| Thermal Shock Resistance, points | 8.5 | |
| 17 to 36 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 2.5 to 3.1 |
| Cobalt (Co), % | 0 | |
| 0.25 to 0.55 |
| Copper (Cu), % | 0 | |
| 92.4 to 95.8 |
| Gold (Au), % | 69.5 to 70.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 21.5 to 22.5 | |
| 0 to 0.2 |
| Palladium (Pd), % | 7.5 to 8.5 | |
| 0 |
| Silicon (Si), % | 0 | |
| 1.5 to 2.1 |
| Zinc (Zn), % | 0 | |
| 0 to 0.8 |
| Residuals, % | 0 | |
| 0 to 0.5 |