AWS BCo-1 vs. AWS BNi-2
AWS BCo-1 belongs to the cobalt alloys classification, while AWS BNi-2 belongs to the nickel alloys. They have a modest 30% of their average alloy composition in common, which, by itself, doesn't mean much. There are 19 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is AWS BCo-1 and the bottom bar is AWS BNi-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 180 |
| Poisson's Ratio | 0.3 | |
| 0.3 |
| Shear Modulus, GPa | 78 | |
| 68 |
| Tensile Strength: Ultimate (UTS), MPa | 700 | |
| 440 |
Thermal Properties
| Brazing Temperature, °C | 1150 to 1230 | |
| 1010 to 1180 |
| Latent Heat of Fusion, J/g | 420 | |
| 360 |
| Melting Completion (Liquidus), °C | 1150 | |
| 1000 |
| Melting Onset (Solidus), °C | 1120 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 490 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 9.3 |
| Embodied Energy, MJ/kg | 110 | |
| 130 |
| Embodied Water, L/kg | 430 | |
| 230 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 12 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 24 | |
| 15 |
| Strength to Weight: Bending, points | 22 | |
| 16 |
| Thermal Shock Resistance, points | 21 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 to 0.050 |
| Boron (B), % | 0.7 to 0.9 | |
| 2.8 to 3.5 |
| Carbon (C), % | 0.35 to 0.45 | |
| 0 to 0.060 |
| Chromium (Cr), % | 18 to 20 | |
| 6.0 to 8.0 |
| Cobalt (Co), % | 46 to 54 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 1.0 | |
| 2.5 to 3.5 |
| Nickel (Ni), % | 16 to 18 | |
| 79.1 to 84.8 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.020 |
| Selenium (Se), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Silicon (Si), % | 7.5 to 8.5 | |
| 4.0 to 5.0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 to 0.050 | |
| 0 to 0.050 |
| Tungsten (W), % | 3.5 to 4.5 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.050 | |
| 0 to 0.050 |
| Residuals, % | 0 | |
| 0 to 0.5 |