AWS BNi-1 vs. Grade 360 Molybdenum

AWS BNi-1 belongs to the nickel alloys classification, while grade 360 molybdenum belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS BNi-1 and the bottom bar is grade 360 molybdenum.

AWS BNi-1 (N99600) Filler Metal Grade 360 Molybdenum

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		180
Elastic (Young's, Tensile) Modulus, GPa		310

Poisson's Ratio		0.3
Poisson's Ratio		0.31

Shear Modulus, GPa		70
Shear Modulus, GPa		120

Tensile Strength: Ultimate (UTS), MPa		450
Tensile Strength: Ultimate (UTS), MPa		430 to 620

Thermal Properties

Latent Heat of Fusion, J/g		360
Latent Heat of Fusion, J/g		370

Specific Heat Capacity, J/kg-K		500
Specific Heat Capacity, J/kg-K		250

Thermal Expansion, µm/m-K		12
Thermal Expansion, µm/m-K		7.0

Otherwise Unclassified Properties

Density, g/cm³		8.0
Density, g/cm³		10

Embodied Carbon, kg CO₂/kg material		8.8
Embodied Carbon, kg CO₂/kg material		28

Embodied Energy, MJ/kg		120
Embodied Energy, MJ/kg		330

Embodied Water, L/kg		240
Embodied Water, L/kg		360

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		17

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		22

Strength to Weight: Axial, points		16
Strength to Weight: Axial, points		12 to 17

Strength to Weight: Bending, points		16
Strength to Weight: Bending, points		12 to 16

Thermal Shock Resistance, points		15
Thermal Shock Resistance, points		14 to 21

Alloy Composition

Aluminum (Al), %		0 to 0.050
Aluminum (Al), %		0

Boron (B), %		2.8 to 3.5
Boron (B), %		0

Carbon (C), %		0.6 to 0.9
Carbon (C), %		0 to 0.030

Chromium (Cr), %		13 to 15
Chromium (Cr), %		0

Cobalt (Co), %		0 to 0.1
Cobalt (Co), %		0

Iron (Fe), %		4.0 to 5.0
Iron (Fe), %		0 to 0.010

Molybdenum (Mo), %		0
Molybdenum (Mo), %		99.9 to 100

Nickel (Ni), %		69.8 to 75.7
Nickel (Ni), %		0 to 0.0020

Nitrogen (N), %		0
Nitrogen (N), %		0 to 0.0020

Oxygen (O), %		0
Oxygen (O), %		0 to 0.0015

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0

Selenium (Se), %		0 to 0.0050
Selenium (Se), %		0

Silicon (Si), %		4.0 to 5.0
Silicon (Si), %		0 to 0.010

Sulfur (S), %		0 to 0.020
Sulfur (S), %		0

Titanium (Ti), %		0 to 0.050
Titanium (Ti), %		0

Zirconium (Zr), %		0 to 0.050
Zirconium (Zr), %		0

Residuals, %		0 to 0.5
Residuals, %		0