AWS BNi-10 belongs to the nickel alloys classification, while EN 1.3536 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS BNi-10 and the bottom bar is EN 1.3536 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 600
660

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Melting Completion (Liquidus), °C 1110
1450
Melting Onset (Solidus), °C 970
1410
Specific Heat Capacity, J/kg-K 440
470
Thermal Expansion, µm/m-K 11
13

Otherwise Unclassified Properties

Base Metal Price, % relative 80
2.9
Density, g/cm3 9.4
7.8
Embodied Carbon, kg CO2/kg material 11
1.6
Embodied Energy, MJ/kg 160
21
Embodied Water, L/kg 230
55

Common Calculations

Stiffness to Weight: Axial, points 12
13
Stiffness to Weight: Bending, points 21
24
Strength to Weight: Axial, points 18
23
Strength to Weight: Bending, points 17
22
Thermal Shock Resistance, points 19
19

Alloy Composition

Aluminum (Al), % 0 to 0.050
0 to 0.050
Boron (B), % 2.0 to 3.0
0
Carbon (C), % 0.4 to 0.55
0.93 to 1.1
Chromium (Cr), % 10 to 13
1.7 to 2.0
Cobalt (Co), % 0 to 0.1
0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 2.5 to 4.5
96 to 97.4
Manganese (Mn), % 0
0.6 to 0.8
Molybdenum (Mo), % 0
0.2 to 0.35
Nickel (Ni), % 57.2 to 67.1
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.020
0 to 0.025
Selenium (Se), % 0 to 0.0050
0
Silicon (Si), % 3.0 to 4.0
0.15 to 0.45
Sulfur (S), % 0 to 0.020
0 to 0.030
Titanium (Ti), % 0 to 0.050
0
Tungsten (W), % 15 to 17
0
Zirconium (Zr), % 0 to 0.050
0
Residuals, % 0 to 0.5
0