AWS BNi-2 vs. AWS E70C-Ni2

AWS BNi-2 belongs to the nickel alloys classification, while AWS E70C-Ni2 belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS BNi-2 and the bottom bar is AWS E70C-Ni2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 180
190
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 68
72
Tensile Strength: Ultimate (UTS), MPa 440
560

Thermal Properties

Latent Heat of Fusion, J/g 360
250
Melting Completion (Liquidus), °C 1000
1450
Melting Onset (Solidus), °C 970
1410
Specific Heat Capacity, J/kg-K 490
470
Thermal Expansion, µm/m-K 11
13

Otherwise Unclassified Properties

Base Metal Price, % relative 55
3.3
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 9.3
1.6
Embodied Energy, MJ/kg 130
22
Embodied Water, L/kg 230
51

Common Calculations

Stiffness to Weight: Axial, points 12
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 15
20
Strength to Weight: Bending, points 16
19
Thermal Shock Resistance, points 16
17

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Boron (B), % 2.8 to 3.5
0
Carbon (C), % 0 to 0.060
0 to 0.080
Chromium (Cr), % 6.0 to 8.0
0
Cobalt (Co), % 0 to 0.1
0
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 2.5 to 3.5
94.1 to 98.3
Manganese (Mn), % 0
0 to 1.3
Nickel (Ni), % 79.1 to 84.8
1.8 to 2.8
Phosphorus (P), % 0 to 0.020
0 to 0.025
Selenium (Se), % 0 to 0.0050
0
Silicon (Si), % 4.0 to 5.0
0 to 0.9
Sulfur (S), % 0 to 0.020
0 to 0.030
Titanium (Ti), % 0 to 0.050
0
Vanadium (V), % 0
0 to 0.030
Zirconium (Zr), % 0 to 0.050
0
Residuals, % 0
0 to 0.5