AWS BNi-4 vs. EN 1.6587 Steel

AWS BNi-4 belongs to the nickel alloys classification, while EN 1.6587 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS BNi-4 and the bottom bar is EN 1.6587 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 180
190
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 67
73
Tensile Strength: Ultimate (UTS), MPa 430
520 to 1420

Thermal Properties

Latent Heat of Fusion, J/g 340
250
Melting Completion (Liquidus), °C 1070
1460
Melting Onset (Solidus), °C 980
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 11
13

Otherwise Unclassified Properties

Base Metal Price, % relative 60
3.8
Density, g/cm3 8.5
7.9
Embodied Carbon, kg CO2/kg material 10
1.7
Embodied Energy, MJ/kg 140
22
Embodied Water, L/kg 220
58

Common Calculations

Stiffness to Weight: Axial, points 12
13
Stiffness to Weight: Bending, points 22
24
Strength to Weight: Axial, points 14
18 to 50
Strength to Weight: Bending, points 15
18 to 36
Thermal Shock Resistance, points 16
15 to 42

Alloy Composition

Aluminum (Al), % 0 to 0.050
0 to 0.050
Boron (B), % 1.5 to 2.2
0
Carbon (C), % 0 to 0.060
0.15 to 0.21
Chromium (Cr), % 0
1.5 to 1.8
Cobalt (Co), % 0 to 0.1
0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 0 to 1.5
94.4 to 96.4
Manganese (Mn), % 0
0.5 to 0.9
Molybdenum (Mo), % 0
0.25 to 0.35
Nickel (Ni), % 91.4 to 95.5
1.4 to 1.7
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.020
0 to 0.025
Selenium (Se), % 0 to 0.0050
0
Silicon (Si), % 3.0 to 4.0
0 to 0.4
Sulfur (S), % 0 to 0.020
0 to 0.030
Titanium (Ti), % 0 to 0.050
0
Zirconium (Zr), % 0 to 0.050
0
Residuals, % 0 to 0.5
0