AWS BNi-4 vs. C82400 Copper
AWS BNi-4 belongs to the nickel alloys classification, while C82400 copper belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is AWS BNi-4 and the bottom bar is C82400 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 120 |
| Poisson's Ratio | 0.31 | |
| 0.33 |
| Shear Modulus, GPa | 67 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 500 to 1030 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 230 |
| Melting Completion (Liquidus), °C | 1070 | |
| 1000 |
| Melting Onset (Solidus), °C | 980 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Expansion, µm/m-K | 11 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 8.9 |
| Embodied Energy, MJ/kg | 140 | |
| 140 |
| Embodied Water, L/kg | 220 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 22 | |
| 19 |
| Strength to Weight: Axial, points | 14 | |
| 16 to 33 |
| Strength to Weight: Bending, points | 15 | |
| 16 to 26 |
| Thermal Shock Resistance, points | 16 | |
| 17 to 36 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 to 0.15 |
| Beryllium (Be), % | 0 | |
| 1.6 to 1.9 |
| Boron (B), % | 1.5 to 2.2 | |
| 0 |
| Carbon (C), % | 0 to 0.060 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Cobalt (Co), % | 0 to 0.1 | |
| 0.2 to 0.65 |
| Copper (Cu), % | 0 | |
| 96 to 98.2 |
| Iron (Fe), % | 0 to 1.5 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Nickel (Ni), % | 91.4 to 95.5 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Selenium (Se), % | 0 to 0.0050 | |
| 0 |
| Silicon (Si), % | 3.0 to 4.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 to 0.050 | |
| 0 to 0.12 |
| Zinc (Zn), % | 0 | |
| 0 to 0.1 |
| Zirconium (Zr), % | 0 to 0.050 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |