AWS BNi-7 vs. N07752 Nickel
Both AWS BNi-7 and N07752 nickel are nickel alloys. They have 88% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is AWS BNi-7 and the bottom bar is N07752 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 170 | |
190 |
Poisson's Ratio | 0.3 | |
0.29 |
Shear Modulus, GPa | 67 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 550 | |
1120 |
Thermal Properties
Latent Heat of Fusion, J/g | 280 | |
310 |
Melting Completion (Liquidus), °C | 890 | |
1380 |
Melting Onset (Solidus), °C | 890 | |
1330 |
Specific Heat Capacity, J/kg-K | 490 | |
460 |
Thermal Expansion, µm/m-K | 11 | |
12 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 55 | |
60 |
Density, g/cm3 | 8.0 | |
8.4 |
Embodied Carbon, kg CO2/kg material | 8.8 | |
10 |
Embodied Energy, MJ/kg | 120 | |
150 |
Embodied Water, L/kg | 240 | |
260 |
Common Calculations
Stiffness to Weight: Axial, points | 12 | |
13 |
Stiffness to Weight: Bending, points | 23 | |
23 |
Strength to Weight: Axial, points | 19 | |
37 |
Strength to Weight: Bending, points | 19 | |
29 |
Thermal Shock Resistance, points | 21 | |
34 |
Alloy Composition
Aluminum (Al), % | 0 to 0.050 | |
0.4 to 1.0 |
Boron (B), % | 0 to 0.010 | |
0 to 0.0070 |
Carbon (C), % | 0 to 0.060 | |
0.020 to 0.060 |
Chromium (Cr), % | 13 to 15 | |
14.5 to 17 |
Cobalt (Co), % | 0 to 0.1 | |
0 to 0.050 |
Copper (Cu), % | 0 | |
0 to 0.5 |
Iron (Fe), % | 0 to 0.2 | |
5.0 to 9.0 |
Manganese (Mn), % | 0 to 0.040 | |
0 to 1.0 |
Nickel (Ni), % | 73.3 to 77.3 | |
70 to 77.1 |
Niobium (Nb), % | 0 | |
0.7 to 1.2 |
Phosphorus (P), % | 9.7 to 10.5 | |
0 to 0.0080 |
Selenium (Se), % | 0 to 0.0050 | |
0 |
Silicon (Si), % | 0 to 0.1 | |
0 to 0.5 |
Sulfur (S), % | 0 to 0.020 | |
0 to 0.0030 |
Titanium (Ti), % | 0 to 0.050 | |
2.3 to 2.8 |
Vanadium (V), % | 0 | |
0 to 0.1 |
Zinc (Zn), % | 0 | |
0 to 0.050 |
Zirconium (Zr), % | 0 to 0.050 | |
0 |
Residuals, % | 0 to 0.5 | |
0 |