AWS BVAg-0 vs. C86500 Bronze

AWS BVAg-0 belongs to the otherwise unclassified metals classification, while C86500 bronze belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is C86500 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
110
Poisson's Ratio 0.37
0.3
Shear Modulus, GPa 26
40
Tensile Strength: Ultimate (UTS), MPa 130
530

Thermal Properties

Latent Heat of Fusion, J/g 110
170
Melting Completion (Liquidus), °C 960
880
Melting Onset (Solidus), °C 960
860
Specific Heat Capacity, J/kg-K 240
390
Thermal Expansion, µm/m-K 20
21

Otherwise Unclassified Properties

Density, g/cm3 10
7.9

Common Calculations

Stiffness to Weight: Axial, points 3.8
7.4
Stiffness to Weight: Bending, points 13
20
Strength to Weight: Axial, points 3.4
19
Strength to Weight: Bending, points 5.4
18
Thermal Shock Resistance, points 6.6
17

Alloy Composition

Aluminum (Al), % 0
0.5 to 1.5
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 0 to 0.050
55 to 60
Iron (Fe), % 0
0.4 to 2.0
Lead (Pb), % 0 to 0.0020
0 to 0.4
Manganese (Mn), % 0
0.1 to 1.5
Nickel (Ni), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 99.95 to 100
0
Tin (Sn), % 0
0 to 1.0
Zinc (Zn), % 0 to 0.0010
36 to 42
Residuals, % 0
0 to 1.0