AWS BVAg-18 vs. SAE-AISI H41 Steel

AWS BVAg-18 belongs to the otherwise unclassified metals classification, while SAE-AISI H41 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-18 and the bottom bar is SAE-AISI H41 steel.

AWS BVAg-18 (P07607) Vacuum Service Filler Metal SAE-AISI H41 (T20841) Molybdenum Hot-Work Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		82
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.36
Poisson's Ratio		0.29

Shear Modulus, GPa		30
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		180
Tensile Strength: Ultimate (UTS), MPa		710 to 2210

Thermal Properties

Latent Heat of Fusion, J/g		140
Latent Heat of Fusion, J/g		270

Melting Completion (Liquidus), °C		720
Melting Completion (Liquidus), °C		1560

Melting Onset (Solidus), °C		600
Melting Onset (Solidus), °C		1510

Specific Heat Capacity, J/kg-K		280
Specific Heat Capacity, J/kg-K		450

Thermal Expansion, µm/m-K		19
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Density, g/cm³		9.7
Density, g/cm³		8.1

Embodied Carbon, kg CO₂/kg material		59
Embodied Carbon, kg CO₂/kg material		6.8

Embodied Energy, MJ/kg		930
Embodied Energy, MJ/kg		97

Common Calculations

Stiffness to Weight: Axial, points		4.7
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		15
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		5.1
Strength to Weight: Axial, points		24 to 76

Strength to Weight: Bending, points		7.3
Strength to Weight: Bending, points		22 to 47

Thermal Shock Resistance, points		8.1
Thermal Shock Resistance, points		20 to 64

Alloy Composition

Cadmium (Cd), %		0 to 0.0010
Cadmium (Cd), %		0

Carbon (C), %		0 to 0.0050
Carbon (C), %		0.6 to 0.75

Chromium (Cr), %		0
Chromium (Cr), %		3.5 to 4.0

Copper (Cu), %		28.5 to 31.5
Copper (Cu), %		0

Iron (Fe), %		0
Iron (Fe), %		81.8 to 85

Lead (Pb), %		0 to 0.0020
Lead (Pb), %		0

Manganese (Mn), %		0
Manganese (Mn), %		0.15 to 0.4

Molybdenum (Mo), %		0
Molybdenum (Mo), %		8.2 to 9.2

Phosphorus (P), %		0 to 0.0020
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0
Silicon (Si), %		0.2 to 0.45

Silver (Ag), %		59 to 61
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030

Tin (Sn), %		9.5 to 10.5
Tin (Sn), %		0

Tungsten (W), %		0
Tungsten (W), %		1.4 to 2.1

Vanadium (V), %		0
Vanadium (V), %		1.0 to 1.3

Zinc (Zn), %		0 to 0.0010
Zinc (Zn), %		0