AWS BVAg-18 vs. N08810 Stainless Steel

AWS BVAg-18 belongs to the otherwise unclassified metals classification, while N08810 stainless steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-18 and the bottom bar is N08810 stainless steel.

AWS BVAg-18 (P07607) Vacuum Service Filler Metal UNS N08810 (Alloy 800H) Stainless Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		82
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.36
Poisson's Ratio		0.28

Shear Modulus, GPa		30
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		180
Tensile Strength: Ultimate (UTS), MPa		520

Thermal Properties

Latent Heat of Fusion, J/g		140
Latent Heat of Fusion, J/g		300

Melting Completion (Liquidus), °C		720
Melting Completion (Liquidus), °C		1400

Melting Onset (Solidus), °C		600
Melting Onset (Solidus), °C		1350

Specific Heat Capacity, J/kg-K		280
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		19
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Density, g/cm³		9.7
Density, g/cm³		8.0

Embodied Carbon, kg CO₂/kg material		59
Embodied Carbon, kg CO₂/kg material		5.3

Embodied Energy, MJ/kg		930
Embodied Energy, MJ/kg		76

Common Calculations

Stiffness to Weight: Axial, points		4.7
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		15
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		5.1
Strength to Weight: Axial, points		18

Strength to Weight: Bending, points		7.3
Strength to Weight: Bending, points		18

Thermal Shock Resistance, points		8.1
Thermal Shock Resistance, points		13

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0.15 to 0.6

Cadmium (Cd), %		0 to 0.0010
Cadmium (Cd), %		0

Carbon (C), %		0 to 0.0050
Carbon (C), %		0.050 to 0.1

Chromium (Cr), %		0
Chromium (Cr), %		19 to 23

Copper (Cu), %		28.5 to 31.5
Copper (Cu), %		0 to 0.75

Iron (Fe), %		0
Iron (Fe), %		39.5 to 50.7

Lead (Pb), %		0 to 0.0020
Lead (Pb), %		0

Manganese (Mn), %		0
Manganese (Mn), %		0 to 1.5

Nickel (Ni), %		0
Nickel (Ni), %		30 to 35

Phosphorus (P), %		0 to 0.0020
Phosphorus (P), %		0 to 0.045

Silicon (Si), %		0
Silicon (Si), %		0 to 1.0

Silver (Ag), %		59 to 61
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.015

Tin (Sn), %		9.5 to 10.5
Tin (Sn), %		0

Titanium (Ti), %		0
Titanium (Ti), %		0.15 to 0.6

Zinc (Zn), %		0 to 0.0010
Zinc (Zn), %		0