AWS BVAg-30 vs. AWS BAg-23
Both AWS BVAg-30 and AWS BAg-23 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 68% of their average alloy composition in common.
For each property being compared, the top bar is AWS BVAg-30 and the bottom bar is AWS BAg-23.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 86 | |
| 90 |
| Poisson's Ratio | 0.36 | |
| 0.36 |
| Shear Modulus, GPa | 31 | |
| 33 |
| Tensile Strength: Ultimate (UTS), MPa | 170 | |
| 170 |
Thermal Properties
| Brazing Temperature, °C | 810 to 930 | |
| 750 to 1040 |
| Latent Heat of Fusion, J/g | 140 | |
| 130 |
| Melting Completion (Liquidus), °C | 810 | |
| 970 |
| Melting Onset (Solidus), °C | 810 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 280 | |
| 270 |
| Thermal Expansion, µm/m-K | 19 | |
| 20 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.7 | |
| 5.0 |
| Stiffness to Weight: Bending, points | 14 | |
| 15 |
| Strength to Weight: Axial, points | 4.7 | |
| 4.7 |
| Strength to Weight: Bending, points | 6.7 | |
| 6.8 |
| Thermal Shock Resistance, points | 7.6 | |
| 6.8 |
Alloy Composition
| Cadmium (Cd), % | 0 to 0.0010 | |
| 0 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 |
| Copper (Cu), % | 25.5 to 28.5 | |
| 0 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 13.9 to 16 |
| Palladium (Pd), % | 4.5 to 5.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 |
| Silver (Ag), % | 67 to 69 | |
| 84 to 86 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |