AWS BVAg-30 belongs to the otherwise unclassified metals classification, while C11100 copper belongs to the copper alloys. They have a modest 27% of their average alloy composition in common, which, by itself, doesn't mean much. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-30 and the bottom bar is C11100 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 86
120
Poisson's Ratio 0.36
0.34
Shear Modulus, GPa 31
44
Tensile Strength: Ultimate (UTS), MPa 170
460

Thermal Properties

Latent Heat of Fusion, J/g 140
210
Melting Completion (Liquidus), °C 810
1080
Melting Onset (Solidus), °C 810
1070
Specific Heat Capacity, J/kg-K 280
390
Thermal Expansion, µm/m-K 19
17

Otherwise Unclassified Properties

Density, g/cm3 10
9.0

Common Calculations

Stiffness to Weight: Axial, points 4.7
7.2
Stiffness to Weight: Bending, points 14
18
Strength to Weight: Axial, points 4.7
14
Strength to Weight: Bending, points 6.7
15
Thermal Shock Resistance, points 7.6
16

Alloy Composition

Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 25.5 to 28.5
99.9 to 100
Lead (Pb), % 0 to 0.0020
0
Palladium (Pd), % 4.5 to 5.5
0
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 67 to 69
0
Zinc (Zn), % 0 to 0.0010
0
Residuals, % 0
0 to 0.1