AWS BVAg-6b vs. 7005 Aluminum
AWS BVAg-6b belongs to the otherwise unclassified metals classification, while 7005 aluminum belongs to the aluminum alloys. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AWS BVAg-6b and the bottom bar is 7005 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 93 | |
| 70 |
| Poisson's Ratio | 0.35 | |
| 0.33 |
| Shear Modulus, GPa | 35 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 200 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 160 | |
| 380 |
| Melting Completion (Liquidus), °C | 870 | |
| 640 |
| Melting Onset (Solidus), °C | 780 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 310 | |
| 880 |
| Thermal Expansion, µm/m-K | 19 | |
| 23 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.7 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 49 | |
| 8.3 |
| Embodied Energy, MJ/kg | 770 | |
| 150 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.3 | |
| 13 |
| Stiffness to Weight: Bending, points | 16 | |
| 47 |
| Strength to Weight: Axial, points | 5.1 | |
| 19 to 38 |
| Strength to Weight: Bending, points | 7.3 | |
| 26 to 41 |
| Thermal Shock Resistance, points | 7.4 | |
| 8.7 to 18 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 91 to 94.7 |
| Cadmium (Cd), % | 0 to 0.0010 | |
| 0 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.060 to 0.2 |
| Copper (Cu), % | 49 to 51 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 | |
| 0 to 0.4 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 1.0 to 1.8 |
| Manganese (Mn), % | 0 | |
| 0.2 to 0.7 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.35 |
| Silver (Ag), % | 49 to 51 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0.010 to 0.060 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 4.0 to 5.0 |
| Zirconium (Zr), % | 0 | |
| 0.080 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |