AWS BVAg-6b vs. AWS BAg-2
Both AWS BVAg-6b and AWS BAg-2 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 61% of their average alloy composition in common.
For each property being compared, the top bar is AWS BVAg-6b and the bottom bar is AWS BAg-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 93 | |
| 82 |
| Poisson's Ratio | 0.35 | |
| 0.32 |
| Shear Modulus, GPa | 35 | |
| 31 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 180 |
Thermal Properties
| Brazing Temperature, °C | 870 to 980 | |
| 700 to 840 |
| Latent Heat of Fusion, J/g | 160 | |
| 130 |
| Melting Completion (Liquidus), °C | 870 | |
| 700 |
| Melting Onset (Solidus), °C | 780 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 310 | |
| 310 |
| Thermal Expansion, µm/m-K | 19 | |
| 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.7 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 49 | |
| 35 |
| Embodied Energy, MJ/kg | 770 | |
| 550 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.3 | |
| 5.1 |
| Stiffness to Weight: Bending, points | 16 | |
| 16 |
| Strength to Weight: Axial, points | 5.1 | |
| 5.6 |
| Strength to Weight: Bending, points | 7.3 | |
| 7.9 |
| Thermal Shock Resistance, points | 7.4 | |
| 7.0 |
Alloy Composition
| Cadmium (Cd), % | 0 to 0.0010 | |
| 17 to 19 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 |
| Copper (Cu), % | 49 to 51 | |
| 25 to 27 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 |
| Silver (Ag), % | 49 to 51 | |
| 34 to 36 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 19 to 23 |
| Residuals, % | 0 | |
| 0 to 0.15 |