AWS BVAg-6b vs. Commercially Pure Palladium
Both AWS BVAg-6b and commercially pure palladium are otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is AWS BVAg-6b and the bottom bar is commercially pure palladium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 93 | |
| 120 |
| Poisson's Ratio | 0.35 | |
| 0.39 |
| Shear Modulus, GPa | 35 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 200 to 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 160 | |
| 160 |
| Melting Completion (Liquidus), °C | 870 | |
| 1550 |
| Melting Onset (Solidus), °C | 780 | |
| 1550 |
| Specific Heat Capacity, J/kg-K | 310 | |
| 240 |
| Thermal Expansion, µm/m-K | 19 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.7 | |
| 12 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.3 | |
| 5.6 |
| Stiffness to Weight: Bending, points | 16 | |
| 14 |
| Strength to Weight: Axial, points | 5.1 | |
| 4.5 to 8.8 |
| Strength to Weight: Bending, points | 7.3 | |
| 6.2 to 9.7 |
| Thermal Shock Resistance, points | 7.4 | |
| 9.8 to 19 |
Alloy Composition
| Cadmium (Cd), % | 0 to 0.0010 | |
| 0 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 |
| Copper (Cu), % | 49 to 51 | |
| 0 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 |
| Palladium (Pd), % | 0 | |
| 99.8 to 100 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 |
| Silver (Ag), % | 49 to 51 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |