AWS BVAg-6b vs. EN 1.4710 Stainless Steel
AWS BVAg-6b belongs to the otherwise unclassified metals classification, while EN 1.4710 stainless steel belongs to the iron alloys. There are 13 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is AWS BVAg-6b and the bottom bar is EN 1.4710 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 93 | |
| 190 |
| Poisson's Ratio | 0.35 | |
| 0.29 |
| Shear Modulus, GPa | 35 | |
| 74 |
Thermal Properties
| Latent Heat of Fusion, J/g | 160 | |
| 290 |
| Melting Completion (Liquidus), °C | 870 | |
| 1430 |
| Melting Onset (Solidus), °C | 780 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 310 | |
| 480 |
| Thermal Expansion, µm/m-K | 19 | |
| 9.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.7 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 49 | |
| 1.8 |
| Embodied Energy, MJ/kg | 770 | |
| 24 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.3 | |
| 14 |
| Stiffness to Weight: Bending, points | 16 | |
| 25 |
Alloy Composition
| Cadmium (Cd), % | 0 to 0.0010 | |
| 0 |
| Carbon (C), % | 0 to 0.0050 | |
| 0.2 to 0.35 |
| Chromium (Cr), % | 0 | |
| 6.0 to 8.0 |
| Copper (Cu), % | 49 to 51 | |
| 0 |
| Iron (Fe), % | 0 | |
| 87.4 to 92.3 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.5 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.15 |
| Nickel (Ni), % | 0 | |
| 0 to 0.5 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 1.0 to 2.5 |
| Silver (Ag), % | 49 to 51 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |