AWS BVAg-6b vs. SAE-AISI H22 Steel

AWS BVAg-6b belongs to the otherwise unclassified metals classification, while SAE-AISI H22 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-6b and the bottom bar is SAE-AISI H22 steel.

AWS BVAg-6b (P07507) Vacuum Service Filler Metal SAE-AISI H22 (T20822) Tungsten Hot-Work Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		93
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.35
Poisson's Ratio		0.29

Shear Modulus, GPa		35
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		180
Tensile Strength: Ultimate (UTS), MPa		700 to 1920

Thermal Properties

Latent Heat of Fusion, J/g		160
Latent Heat of Fusion, J/g		250

Melting Completion (Liquidus), °C		870
Melting Completion (Liquidus), °C		1670

Melting Onset (Solidus), °C		780
Melting Onset (Solidus), °C		1620

Specific Heat Capacity, J/kg-K		310
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		19
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Density, g/cm³		9.7
Density, g/cm³		8.7

Embodied Carbon, kg CO₂/kg material		49
Embodied Carbon, kg CO₂/kg material		4.9

Embodied Energy, MJ/kg		770
Embodied Energy, MJ/kg		73

Common Calculations

Stiffness to Weight: Axial, points		5.3
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		16
Stiffness to Weight: Bending, points		22

Strength to Weight: Axial, points		5.1
Strength to Weight: Axial, points		22 to 61

Strength to Weight: Bending, points		7.3
Strength to Weight: Bending, points		20 to 39

Thermal Shock Resistance, points		7.4
Thermal Shock Resistance, points		22 to 60

Alloy Composition

Cadmium (Cd), %		0 to 0.0010
Cadmium (Cd), %		0

Carbon (C), %		0 to 0.0050
Carbon (C), %		0.3 to 0.4

Chromium (Cr), %		0
Chromium (Cr), %		1.8 to 3.8

Copper (Cu), %		49 to 51
Copper (Cu), %		0 to 0.25

Iron (Fe), %		0
Iron (Fe), %		82.2 to 87.4

Lead (Pb), %		0 to 0.0020
Lead (Pb), %		0

Manganese (Mn), %		0
Manganese (Mn), %		0.15 to 0.4

Nickel (Ni), %		0
Nickel (Ni), %		0 to 0.3

Phosphorus (P), %		0 to 0.0020
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0
Silicon (Si), %		0.15 to 0.4

Silver (Ag), %		49 to 51
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030

Tungsten (W), %		0
Tungsten (W), %		10 to 11.8

Vanadium (V), %		0
Vanadium (V), %		0.25 to 0.5

Zinc (Zn), %		0 to 0.0010
Zinc (Zn), %		0