AWS BVAg-8 vs. AWS BVAg-8b
Both AWS BVAg-8 and AWS BVAg-8b are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. Their average alloy composition is basically identical.
For each property being compared, the top bar is AWS BVAg-8 and the bottom bar is AWS BVAg-8b.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 84 | |
| 84 |
| Poisson's Ratio | 0.36 | |
| 0.36 |
| Shear Modulus, GPa | 31 | |
| 31 |
| Tensile Strength: Ultimate (UTS), MPa | 170 | |
| 170 |
Thermal Properties
| Brazing Temperature, °C | 780 to 900 | |
| 800 to 900 |
| Latent Heat of Fusion, J/g | 140 | |
| 140 |
| Melting Completion (Liquidus), °C | 780 | |
| 800 |
| Melting Onset (Solidus), °C | 780 | |
| 780 |
| Specific Heat Capacity, J/kg-K | 280 | |
| 280 |
| Thermal Expansion, µm/m-K | 19 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.6 | |
| 4.7 |
| Stiffness to Weight: Bending, points | 14 | |
| 15 |
| Strength to Weight: Axial, points | 4.7 | |
| 4.7 |
| Strength to Weight: Bending, points | 6.8 | |
| 6.8 |
| Thermal Shock Resistance, points | 7.6 | |
| 7.6 |
Alloy Composition
| Cadmium (Cd), % | 0 to 0.0010 | |
| 0 to 0.0010 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Copper (Cu), % | 27 to 29 | |
| 26.8 to 29.2 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 to 0.0020 |
| Nickel (Ni), % | 0 | |
| 0.3 to 0.7 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 to 0.0020 |
| Silver (Ag), % | 71 to 73 | |
| 70.5 to 72.5 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 to 0.0010 |