AWS BVAg-8b belongs to the otherwise unclassified metals classification, while AWS E16-8-2 belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-8b and the bottom bar is AWS E16-8-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 84
200
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 31
77
Tensile Strength: Ultimate (UTS), MPa 170
620

Thermal Properties

Latent Heat of Fusion, J/g 140
280
Melting Completion (Liquidus), °C 800
1440
Melting Onset (Solidus), °C 780
1400
Specific Heat Capacity, J/kg-K 280
470
Thermal Expansion, µm/m-K 19
14

Otherwise Unclassified Properties

Density, g/cm3 10
7.9

Common Calculations

Stiffness to Weight: Axial, points 4.7
14
Stiffness to Weight: Bending, points 15
25
Strength to Weight: Axial, points 4.7
22
Strength to Weight: Bending, points 6.8
20
Thermal Shock Resistance, points 7.6
16

Alloy Composition

Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0 to 0.1
Chromium (Cr), % 0
14.5 to 16.5
Copper (Cu), % 26.8 to 29.2
0 to 0.75
Iron (Fe), % 0
68 to 76.5
Lead (Pb), % 0 to 0.0020
0
Manganese (Mn), % 0
0.5 to 2.5
Molybdenum (Mo), % 0
1.0 to 2.0
Nickel (Ni), % 0.3 to 0.7
7.5 to 9.5
Phosphorus (P), % 0 to 0.0020
0 to 0.030
Silicon (Si), % 0
0 to 0.6
Silver (Ag), % 70.5 to 72.5
0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.0010
0