AWS BVAg-8b vs. N10629 Nickel
AWS BVAg-8b belongs to the otherwise unclassified metals classification, while N10629 nickel belongs to the nickel alloys. There are 15 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is AWS BVAg-8b and the bottom bar is N10629 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 84 | |
| 220 |
| Poisson's Ratio | 0.36 | |
| 0.31 |
| Shear Modulus, GPa | 31 | |
| 83 |
| Tensile Strength: Ultimate (UTS), MPa | 170 | |
| 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 310 |
| Melting Completion (Liquidus), °C | 800 | |
| 1610 |
| Melting Onset (Solidus), °C | 780 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 280 | |
| 390 |
| Thermal Expansion, µm/m-K | 19 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 9.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.7 | |
| 13 |
| Stiffness to Weight: Bending, points | 15 | |
| 22 |
| Strength to Weight: Axial, points | 4.7 | |
| 26 |
| Strength to Weight: Bending, points | 6.8 | |
| 22 |
| Thermal Shock Resistance, points | 7.6 | |
| 27 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.1 to 0.5 |
| Cadmium (Cd), % | 0 to 0.0010 | |
| 0 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 to 0.010 |
| Chromium (Cr), % | 0 | |
| 0.5 to 1.5 |
| Cobalt (Co), % | 0 | |
| 0 to 2.5 |
| Copper (Cu), % | 26.8 to 29.2 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 | |
| 1.0 to 6.0 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 26 to 30 |
| Nickel (Ni), % | 0.3 to 0.7 | |
| 65 to 72.4 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 0.050 |
| Silver (Ag), % | 70.5 to 72.5 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |