AWS BVAu-2 vs. 1230A Aluminum

AWS BVAu-2 belongs to the otherwise unclassified metals classification, while 1230A aluminum belongs to the aluminum alloys. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS BVAu-2 and the bottom bar is 1230A aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
69
Poisson's Ratio 0.4
0.33
Shear Modulus, GPa 36
26
Tensile Strength: Ultimate (UTS), MPa 150
89 to 170

Thermal Properties

Latent Heat of Fusion, J/g 92
400
Melting Completion (Liquidus), °C 890
640
Melting Onset (Solidus), °C 890
640
Specific Heat Capacity, J/kg-K 180
900
Thermal Expansion, µm/m-K 15
23

Otherwise Unclassified Properties

Density, g/cm3 17
2.7

Common Calculations

Stiffness to Weight: Axial, points 3.3
14
Stiffness to Weight: Bending, points 9.1
50
Strength to Weight: Axial, points 2.4
9.1 to 17
Strength to Weight: Bending, points 3.6
16 to 25
Thermal Shock Resistance, points 7.1
4.0 to 7.6

Alloy Composition

Aluminum (Al), % 0
99.3 to 100
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 19.5 to 20.5
0 to 0.1
Gold (Au), % 79.5 to 80.5
0
Iron (Fe), % 0
0 to 0.7
Lead (Pb), % 0 to 0.0020
0
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0
0 to 0.050
Phosphorus (P), % 0 to 0.0020
0
Silicon (Si), % 0
0 to 0.7
Zinc (Zn), % 0 to 0.0010
0 to 0.050