AWS BVAu-4 vs. N06230 Nickel

AWS BVAu-4 belongs to the otherwise unclassified metals classification, while N06230 nickel belongs to the nickel alloys. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is AWS BVAu-4 and the bottom bar is N06230 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
210
Poisson's Ratio 0.4
0.28
Shear Modulus, GPa 41
83
Tensile Strength: Ultimate (UTS), MPa 190
620 to 840

Thermal Properties

Latent Heat of Fusion, J/g 100
310
Melting Completion (Liquidus), °C 950
1370
Melting Onset (Solidus), °C 950
1300
Specific Heat Capacity, J/kg-K 190
420
Thermal Expansion, µm/m-K 14
13

Otherwise Unclassified Properties

Density, g/cm3 17
9.5

Common Calculations

Stiffness to Weight: Axial, points 3.6
12
Stiffness to Weight: Bending, points 9.3
21
Strength to Weight: Axial, points 3.0
18 to 25
Strength to Weight: Bending, points 4.2
17 to 21
Thermal Shock Resistance, points 8.7
17 to 23

Alloy Composition

Aluminum (Al), % 0
0.2 to 0.5
Boron (B), % 0
0 to 0.015
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0.050 to 0.15
Chromium (Cr), % 0
20 to 24
Cobalt (Co), % 0
0 to 5.0
Gold (Au), % 81.5 to 82.5
0
Iron (Fe), % 0
0 to 3.0
Lanthanum (La), % 0
0.0050 to 0.050
Lead (Pb), % 0 to 0.0020
0
Manganese (Mn), % 0
0.3 to 1.0
Molybdenum (Mo), % 0
1.0 to 3.0
Nickel (Ni), % 17.5 to 18.5
47.5 to 65.2
Phosphorus (P), % 0 to 0.0020
0 to 0.030
Silicon (Si), % 0
0.25 to 0.75
Sulfur (S), % 0
0 to 0.015
Tungsten (W), % 0
13 to 15
Zinc (Zn), % 0 to 0.0010
0