AWS BVAu-7 vs. EN 1.1191 Steel
AWS BVAu-7 belongs to the otherwise unclassified metals classification, while EN 1.1191 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is AWS BVAu-7 and the bottom bar is EN 1.1191 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 130 | |
190 |
Poisson's Ratio | 0.38 | |
0.29 |
Shear Modulus, GPa | 45 | |
72 |
Tensile Strength: Ultimate (UTS), MPa | 200 | |
630 to 700 |
Thermal Properties
Latent Heat of Fusion, J/g | 140 | |
250 |
Melting Completion (Liquidus), °C | 1120 | |
1460 |
Melting Onset (Solidus), °C | 1100 | |
1420 |
Specific Heat Capacity, J/kg-K | 240 | |
470 |
Thermal Expansion, µm/m-K | 13 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 15 | |
7.8 |
Common Calculations
Stiffness to Weight: Axial, points | 4.7 | |
13 |
Stiffness to Weight: Bending, points | 11 | |
24 |
Strength to Weight: Axial, points | 3.7 | |
22 to 25 |
Strength to Weight: Bending, points | 5.1 | |
21 to 22 |
Thermal Shock Resistance, points | 8.9 | |
20 to 22 |
Alloy Composition
Cadmium (Cd), % | 0 to 0.0010 | |
0 |
Carbon (C), % | 0 to 0.0050 | |
0.42 to 0.5 |
Chromium (Cr), % | 0 | |
0 to 0.4 |
Cobalt (Co), % | 0 to 0.060 | |
0 |
Gold (Au), % | 49.5 to 50.5 | |
0 |
Iron (Fe), % | 0 | |
97.3 to 99.08 |
Lead (Pb), % | 0 to 0.0020 | |
0 |
Manganese (Mn), % | 0 | |
0.5 to 0.8 |
Molybdenum (Mo), % | 0 | |
0 to 0.1 |
Nickel (Ni), % | 24.5 to 25.5 | |
0 to 0.4 |
Palladium (Pd), % | 23.9 to 26 | |
0 |
Phosphorus (P), % | 0 to 0.0020 | |
0 to 0.035 |
Silicon (Si), % | 0 | |
0 to 0.4 |
Sulfur (S), % | 0 | |
0 to 0.035 |
Zinc (Zn), % | 0 to 0.0010 | |
0 |