AWS BVAu-7 vs. C95410 Bronze
AWS BVAu-7 belongs to the otherwise unclassified metals classification, while C95410 bronze belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is AWS BVAu-7 and the bottom bar is C95410 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 120 |
| Poisson's Ratio | 0.38 | |
| 0.34 |
| Shear Modulus, GPa | 45 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 200 | |
| 620 to 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 230 |
| Melting Completion (Liquidus), °C | 1120 | |
| 1040 |
| Melting Onset (Solidus), °C | 1100 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 440 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 15 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.7 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 11 | |
| 20 |
| Strength to Weight: Axial, points | 3.7 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 5.1 | |
| 20 to 22 |
| Thermal Shock Resistance, points | 8.9 | |
| 22 to 26 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 10 to 11.5 |
| Cadmium (Cd), % | 0 to 0.0010 | |
| 0 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 |
| Cobalt (Co), % | 0 to 0.060 | |
| 0 |
| Copper (Cu), % | 0 | |
| 83 to 85.5 |
| Gold (Au), % | 49.5 to 50.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 3.0 to 5.0 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 24.5 to 25.5 | |
| 1.5 to 2.5 |
| Palladium (Pd), % | 23.9 to 26 | |
| 0 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |