AWS BVAu-8 vs. 50Cr-50Ni Alloy
Both AWS BVAu-8 and 50Cr-50Ni alloy are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 13 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AWS BVAu-8 and the bottom bar is 50Cr-50Ni alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 210 |
| Poisson's Ratio | 0.42 | |
| 0.26 |
| Shear Modulus, GPa | 36 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 140 | |
| 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 71 | |
| 350 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 490 |
| Thermal Expansion, µm/m-K | 14 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 19 | |
| 8.0 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.0 | |
| 15 |
| Stiffness to Weight: Bending, points | 8.3 | |
| 25 |
| Strength to Weight: Axial, points | 2.1 | |
| 21 |
| Strength to Weight: Bending, points | 3.2 | |
| 20 |
| Thermal Shock Resistance, points | 7.1 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.25 |
| Cadmium (Cd), % | 0 to 0.0010 | |
| 0 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 48 to 52 |
| Gold (Au), % | 91 to 93 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0 to 1.0 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0 | |
| 44.5 to 52 |
| Nitrogen (N), % | 0 | |
| 0 to 0.3 |
| Palladium (Pd), % | 7.0 to 9.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 | |
| 0 to 0.5 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |