AWS E100C-K3 vs. EN 1.4913 Stainless Steel
Both AWS E100C-K3 and EN 1.4913 stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AWS E100C-K3 and the bottom bar is EN 1.4913 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 18 | |
14 to 22 |
Poisson's Ratio | 0.29 | |
0.28 |
Shear Modulus, GPa | 73 | |
75 |
Tensile Strength: Ultimate (UTS), MPa | 770 | |
870 to 980 |
Tensile Strength: Yield (Proof), MPa | 700 | |
480 to 850 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
270 |
Melting Completion (Liquidus), °C | 1460 | |
1460 |
Melting Onset (Solidus), °C | 1410 | |
1410 |
Specific Heat Capacity, J/kg-K | 470 | |
480 |
Thermal Conductivity, W/m-K | 48 | |
24 |
Thermal Expansion, µm/m-K | 13 | |
11 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.9 | |
2.9 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 9.0 | |
3.3 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 3.4 | |
9.0 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.7 | |
2.9 |
Embodied Energy, MJ/kg | 23 | |
41 |
Embodied Water, L/kg | 53 | |
97 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
130 to 160 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 1290 | |
600 to 1860 |
Stiffness to Weight: Axial, points | 13 | |
14 |
Stiffness to Weight: Bending, points | 24 | |
25 |
Strength to Weight: Axial, points | 27 | |
31 to 35 |
Strength to Weight: Bending, points | 24 | |
26 to 28 |
Thermal Diffusivity, mm2/s | 13 | |
6.5 |
Thermal Shock Resistance, points | 23 | |
31 to 34 |
Alloy Composition
Aluminum (Al), % | 0 | |
0 to 0.020 |
Boron (B), % | 0 | |
0 to 0.0015 |
Carbon (C), % | 0 to 0.15 | |
0.17 to 0.23 |
Chromium (Cr), % | 0 to 0.15 | |
10 to 11.5 |
Copper (Cu), % | 0 to 0.35 | |
0 |
Iron (Fe), % | 92.6 to 98.5 | |
84.5 to 88.3 |
Manganese (Mn), % | 0.75 to 2.3 | |
0.4 to 0.9 |
Molybdenum (Mo), % | 0.25 to 0.65 | |
0.5 to 0.8 |
Nickel (Ni), % | 0.5 to 2.5 | |
0.2 to 0.6 |
Niobium (Nb), % | 0 | |
0.25 to 0.55 |
Nitrogen (N), % | 0 | |
0.050 to 0.1 |
Phosphorus (P), % | 0 to 0.025 | |
0 to 0.025 |
Silicon (Si), % | 0 to 0.8 | |
0 to 0.5 |
Sulfur (S), % | 0 to 0.025 | |
0 to 0.015 |
Vanadium (V), % | 0 to 0.030 | |
0.1 to 0.3 |
Residuals, % | 0 to 0.5 | |
0 |